Code | Orthoclase |
Mineral Group | Alkali Feldspar |
Mineral Class | Framework Silicate |
Formula | KAlSi3O8 |
Occurrence | In all sedimentary rocks. |
Electron Density, calculated from formula (Rhoe_Calc) | 2.55 |
Litho Density, calculated from formula (Rhol_Calc) | 2.54 |
Gamma Ray, measured empirically (Gr_Meas) | 171.00 |
Photoelectric Factor, calculated from formula (Pef_Calc) | 2.86 |
Photoelectric Factor, measured empirically (Pef_Meas) | 3.40 |
Volumetric Photoelectric Factor, calculated from formula (Uma_Calc) | 7.29 |
Neutron Cross-section, calculated from formula (Sigma_Calc) | 15.82 |
Neutron Cross-section, measured empirically (Sigma_Meas) | 15.30 |
Neutron slowing-down length, calculated from formula (Ls_Calc) | 32.13 |
Neutron diffusion length, calculated from formula (Ld_Calc) | 10.69 |
Epithermal CNL porosity, calculated from formula (Epi_Calc) | -1.50 |
Epithermal CNL porosity, measured empirically (Epi_Meas) | -1.00 |
Thermal CNL porosity, calculated from formula (Therm_Calc) | -1.10 |
Thermal CNL porosity, measured empirically (Therm_Meas) | -0.60 |
Bulk Modulus, calculated from formula (Bmod_Calc) | |
Shear Modulus, calculated from formula (Smod_Calc) | |
Delta-T Compressional (us/m), calculated from formula (Dtc_Calc) | 226.40 |
Delta-T Shear (us/m), calculated from formula (Dts_Calc) | |
Poisson's Ratio, calculated from formula (Pr_Calc) | |
EPT Propagation time, calculated from formula (Tp_Calc) | 8.00 |
Molecular weight, calculated from formula (Mol_Wt_Calc) | 278.35 |
Bulk Density, calculated from formula (Rho_Calc) | 2.57 |
Weight % of Hydrogen, calculated from formula (H_Calc) | |
Weight % of Carbon, calculated from formula (C_Calc) | |
Weight % of Oxygen, calculated from formula (O_Calc) | 46.00 |
Weight % of Sodium, calculated from formula (Na_Calc) | |
Weight % of Sodium, measured empirically (Na_Meas) | 2.00 |
Weight % of Magnesium, calculated from formula (Mg_Calc) | |
Weight % of Magnesium, measured empirically (Mg_Meas) | 0.00 |
Weight % of Aluminum, calculated from formula (Al_Calc) | 9.70 |
Weight % of Aluminum, measured empirically (Al_Meas) | 10.00 |
Weight % of Silicon, calculated from formula (Si_Calc) | 30.30 |
Weight % of Silicon, measured empirically (Si_Meas) | 30.00 |
Weight % of Potassium, calculated from formula (K_Calc) | 14.00 |
Weight % of Potassium, measured empirically (K_Meas) | 10.20 |
Weight % of Calcium, calculated from formula (Ca_Calc) | |
Weight % of Calcium, measured empirically (Ca_Meas) | 0.10 |
Weight % of Iron, calculated from formula (Fe_Calc) | |
Weight % of Iron, measured empirically (Fe_Meas) | 0.20 |
Weight % of Boron, calculated from formula (B_Calc) | |
Boron concentration (ppm), measured empirically (B_Meas) | 21.00 |
Weight % of Nitrogen, calculated from formula (N_Calc) | |
Weight % of Fluorine, calculated from formula (F_Calc) | |
Weight % of Phosphorus, calculated from formula (P_Calc) | |
Weight % of Sulfur, calculated from formula (S_Calc) | |
Weight % of Sulfur, measured empirically (S_Meas) | 0.00 |
Weight % of Chlorine, calculated from formula (Cl_Calc) | |
Weight % of Titanium, calculated from formula (Ti_Calc) | |
Weight % of Titanium, measured empirically (Ti_Meas) | 0.01 |
Weight % of Manganese, calculated from formula (Mn_Calc) | |
Weight % of Copper, calculated from formula (Cu_Calc) | |
Weight % of Zinc, calculated from formula (Zn_Calc) | |
Weight % of Strontium, calculated from formula (Sr_Calc) | |
Weight % of Zirconium, calculated from formula (Zr_Calc) | |
Weight % of Barium, calculated from formula (Ba_Calc) | |
Weight % of Lead, calculated from formula (Pb_Calc) | |
Thorium concentration (ppm), measured empirically (Th_Meas) | 1.10 |
Uranium concentration (ppm), measured empirically (U_Meas) | 0.40 |
Gadolinium concentration (ppm), measured empirically (Gd_Meas) | 0.30 |
Loss on Ignition, % weight, measured empirically (Loi_Meas) | 0.50 |
Volatile H component of LOI(H2O+), measured empirically (H_Loi_Meas) | 0.40 |
Trace Elements | Na->5 Th:3->7ppm U:0.2->3ppm Ca,Fe |
Description | |